Gas sensor and method of making

ABSTRACT

A gas sensor is disclosed. The gas sensor includes a gas sensing layer, at least one electrode, an adhesion layer, and a response modification layer adjacent to said gas sensing layer and said layer of adhesion. A system having an exhaust system and a gas sensor is also disclosed. A method of fabricating the gas sensor is also disclosed.

BACKGROUND

The invention relates generally to the area of gas sensing. Morespecifically, the invention relates to the sensing of NO_(x) gas.

Environmental considerations are the primary motivating factors todevelop NO_(x) sensors. NO_(x) emissions react with gases such as SOx,CO and moisture (water vapor) in the air to produce smog and acid rain.One of the major sources of NO_(x) emissions is internal combustionengine exhaust.

The European Euro VI emission standards for light commercial vehicles(category N1-I, N1-II and N1-III, to be implemented by September 2015,require NO_(x) emission levels below 0.5 gm/hp-hr. This typicallytranslates to less than 50 ppm of NO_(x) tail pipe emissions.Development of cost-effective sensors that can give reliable readout atsuch low concentration levels of analyte, and which can deliver robustperformance even in harsh environments, is one of the major challengesfacing present day emissions monitoring technology.

The current paradigm in improving the efficiency of internal combustionengines utilizes the technology of lean burn, whereby very high air:fuelratios (˜10²:1), as compared to conventional stoichiometric ratio(typically ˜20:1), are used. While the lean burn technology improves theefficiency of the engine, it also results in higher NO_(x) emissions.

Any emissions control scheme that adversely impacts or limits efficiencywill not be commercially viable. This necessitates real time monitoringof NO_(x) emission levels and use of this information to dynamicallycontrol engine operating parameters (such as compression ratio, etc.)and exhaust after-treatment systems (such as catalytic filters, etc.) toachieve optimal engine efficiency and optimal emissions control,respectively.

One of current NO_(x) gas sensing technology in the market employsyttria stabilized zirconia (YSZ) based sensors. The sensors areessentially a multi-chamber electrochemical cell measuring the oxygenchanges as a result of NO_(x) decomposition. Such technology requirescatalysts such as platinum (Pt). However, the performance of thecatalyst degrades upon exposure to SO_(x) and water vapor, commonlypresent in the exhaust from internal combustion engine. This is one ofthe factors contributing to lowering the working life of such sensors.Further, the relatively intricate design of such sensors makes themexpensive to replace on a regular basis.

Another current gas sensing technology in the market employssemiconductor sensors. As with any technology, this technology presentssituation specific disadvantages and advantages. For example, gasemissions monitoring applications often require quantitative estimationof a particular or few gas species (e.g., NO_(x)) in a multiple gasspecies environment. Such semiconductor sensors, however, are sensitiveto a broad range of gases, and therefore are of limited utility in suchNO_(x) gas sensing applications. Furthermore, these sensors are prone tolong term instability because of their polycrystalline nature. On theother hand, this technology has the advantages of being solid-state,such as rigid construction and compact size. Further, the technology isamenable to readout using simple electronics, thereby reducing cost ofsystem manufacture, operation, maintenance and replacement. In addition,semiconductor sensors allow a wide range of response tunability viaintroduction of suitable dopants, control of morphology of gas sensingsurface, control of gas sensor operating parameters, amongst othercontrollable factors.

A gas sensor that is semiconductor based, can make quantitativeestimation of NO_(x) gas even at low concentration levels, and has along working life, would, therefore, be highly desirable.

BRIEF DESCRIPTION

Embodiments of the invention are directed towards a gas sensor and amethod for making the gas sensor.

In accordance with one exemplary embodiment of the invention, a gassensor is disclosed. The gas sensor includes a gas sensing layer, atleast one electrode, an adhesion layer, and a response modificationlayer adjacent to said gas sensing layer and said layer of adhesion.

In accordance with one exemplary embodiment of the invention, a systemincluding a system for gas sensing is provided. The system includes anexhaust system to transport gases, and a gas sensor. The gas sensorincludes a gas sensing layer, at least one electrode, an adhesion layer,and a response modification layer adjacent to said gas sensing layer andsaid layer of adhesion.

In accordance with one exemplary embodiment of the invention, a methodfor making a gas sensor is provided. The method includes disposing abeating layer, disposing a first glass layer adjacent to the heatinglayer, disposing a temperature sensing layer adjacent to the first glasslayer, disposing a second glass layer adjacent to the temperaturesensing layer, disposing at least one electrode adjacent to the secondglass layer, disposing an adhesion layer adjacent to the at least oneelectrode, disposing a response modification layer adjacent to theadhesion layer, and disposing a gas sensing layer adjacent to theresponse modification layer.

In accordance with one exemplary embodiment of the invention, a gassensor is disclosed. The gas sensor includes a gas sensing layerincluding at least one metal oxide compound and at least two dopantspecies, wherein the metal is a chemical element selected from the groupconsisting of W, Ta, and Nb, and wherein the dopant species is achemical element selected from the group consisting of Re, Ni, V, Ta,Nb, Mo, and Zr. The gas sensing layer is capable to detecting at leastone analyte selected from the group NO, NO₂, NH₃, H₂O, and combinationsthereof in harsh environments. The gas sensor includes at least oneelectrode in communication with said sensing layer, an adhesion layerincluding a chemical element selected from the group consisting of Ti,Cr, and combinations thereof, and a response modification layerincluding at least one chemical element selected from the list Ti, Re,Ni, Ta, Nb, Mo, Zr, and combinations thereof. The response modificationlayer is adjacent to said gas sensing layer and said layer of adhesion.

These and other advantages and features will be more readily understoodfrom the following detailed description of preferred embodiments of theinvention that is provided in connection with the accompanying drawings.

DRAWINGS

FIG. 1 is a diagrammatical representation of a cross-sectional view of aNO_(x) gas sensor in accordance with an exemplary embodiment of theinvention.

FIG. 2 is a diagrammatical representation of the top view ofinterdigitated electrodes in a NO_(x) gas sensor, in accordance with anexemplary embodiment of the invention.

FIG. 3 is a diagrammatical representation of the top view of inlineelectrodes in a NO_(x) gas sensor, in accordance with another exemplaryembodiment of the invention.

FIG. 4 is a diagrammatical representation of the placement of theelectrodes on a sensing layer of the gas sensor wherein the electrodesare placed in a side-by-side geometry, in accordance with anotherexemplary embodiment of the invention.

FIG. 5 is a diagrammatical representation of the placement of theelectrodes on a sensing layer of the gas sensor wherein the electrodesare placed in a embedded geometry, in accordance with another exemplaryembodiment of the invention.

FIG. 6 is a diagrammatical representation of the placement of theelectrodes on a sensing layer of the gas sensor wherein the electrodesare placed in a extremity geometry, in accordance with another exemplaryembodiment of the invention.

FIG. 7 is a flow chart representation of a manufacturing process of aNO_(x) gas sensor in accordance with an exemplary embodiment of theinvention.

FIG. 8 is a flow chart representation of a method for detecting theanalyte in accordance with one exemplary embodiment of the invention.

FIG. 9 is a graphical representation of the variation in gas sensorresponse upon exposure to 50 ppm NO gas level and 50 ppm NO₂ gas level,wherein the dopant species in a gas sensing layer of the gas sensor isRe, in accordance with one exemplary embodiment of the invention.

FIG. 10 is a graphical representation of the variation in gas sensorresponse upon exposure to different indicated NO and NO₂ gas levels,wherein the dopant species in a gas sensing layer of the gas sensor isV, in accordance with one exemplary embodiment of the invention.

FIG. 11 is a graphical representation of the variation in gas sensorresponse upon exposure to 50 ppm NO gas level and 50 ppm NO₂ gas level,wherein two dopant species Re and V are incorporated in a gas sensinglayer of the gas sensor, in accordance with one exemplary embodiment ofthe invention.

FIG. 12 is a graphical representation of the variation in gas sensorresponse upon exposure to 50 ppm NO gas level and 50 ppm NO₂ gas level,wherein two dopant species Zr and Re are incorporated in a gas sensinglayer of the gas sensor, in accordance with one exemplary embodiment ofthe invention.

FIG. 13 is a graphical representation of the variation in gas sensorresponse upon exposure to 50 ppm NO gas level and 50 ppm NO₂ gas level,wherein two dopant species Ta and Re are incorporated in a gas sensinglayer of the gas sensor, in accordance with one exemplary embodiment ofthe invention.

FIG. 14 is a graphical representation of the variation in gas sensorresponse upon exposure to different indicated NO and NO₂ gas levels,wherein the dopant species in a gas sensing layer of the gas sensor isV, in accordance with one exemplary embodiment of the invention.

FIG. 15 is a graphical representation of the variation in gas sensorresponse upon exposure to different indicated NO and NO₂ gas levels,wherein the dopant species in a gas sensing layer of the sensor is V, inaccordance with one exemplary embodiment of the invention.

FIG. 16 is a graphical representation of the variation in gas sensorresponse upon exposure to different indicated NO and NO₂ gas levels,wherein two dopant species V and Re are incorporated in a gas sensinglayer of the gas sensor, in accordance with one exemplary embodiment ofthe invention.

FIG. 17 is a graphical, representation of the variation in gas sensorresponse upon exposure to different indicated NO and NO₂ gas levels,wherein two dopant species V and Re are incorporated in a gas sensinglayer of the gas sensor, in accordance with one exemplary embodiment ofthe invention.

DETAILED DESCRIPTION

In the following description, whenever a particular aspect or feature ofthe invention is said to comprise or consist of at least one element ofa group and combinations thereof, it is understood that the aspect orfeature may comprise or consist of any of the elements of the group,either individually or in combination with any of the other elements ofthat group.

In the following specification and the claims that follow, the singularforms “a”, “an” and “the” include plural referents unless the contextclearly dictates otherwise.

A gas sensor may be used to determine if an “analyte” is present and/orto quantify an amount of the analyte. As used herein, the term “analyte”may refer to any substance to be detected and/or quantified, includingbut not limited to a gas, a vapor, a bioanalyte, particulate matter, anda combination thereof.

Since the primary constituents of NO_(x), i.e., NO and NO₂ areinterconvertible, reliable estimation of total NO_(x) may be achieved ifthe response of the gas sensor, i.e., the NO_(x) concentration dependentchange in resistance of the gas sensor is equal (in terms of magnitudeand sign) for both NO and NO₂. Thus, if ΔR(NO₂, c) and ΔR(NO, c) be theresponse of the sensor to concentration “c” of NO₂ and NO respectively,then a response ratio “rr” (defined below) close to unity would bedesirable.

rr=ΔR(NO₂ ,c)/ΔR(NO,c)  (1)

As used herein, the term “equisensitivity” refers to “rr” definedaccording to equation (1) when it is in a range from about 0.5 to about3.

As used herein, the term “adjacent,” when used in context of discussionof different components comprising the gas sensor refers to “immediatelynext to” or it refers to the situation wherein other components presentbetween the components under discussion.

As used herein, the term “communication,” when used in context ofdiscussion of more than one component comprising the gas sensor may meanthat any change in an electrical characteristic of one component isreflected at, and therefore, detectable and measurable via, the othercomponent.

As used herein, the term “self-consistent,” when used in the context ofdiscussion of the chemical formula of a chemical compound composing ahost component of a gas sensing layer of a gas sensor may mean that thesaid chemical formula is consistent with established scientificprinciples that would be known to one skilled in the art. Necessarilyimplied in the said definition of the term “self-consistent” is thesituation wherein the said chemical formula represents a metal oxideinorganic compound. In other words, the said chemical formula mustrepresent an inorganic metal oxide chemical composition. A generalexample of chemical formula of host component of the gas sensor may beTa₂O₅, WO_(2,9).

As used herein, the term “thin film,” when used in the context ofdiscussion of the gas sensing layer of a gas sensor refers to thesituation wherein the thickness of the said gas sensing layer is fromabout 10 nm to about 500 nm.

As used herein, the term “thick film,” when used in the context ofdiscussion of the gas sensing layer of a gas sensor refers to thesituation wherein the thickness of the said gas sensing layer is fromabout 500 nm to about 500 μm.

As used herein, the term “pellet”, when used in the context ofdiscussion of the gas sensing layer of a gas sensor refers to thesituation wherein the thickness of the said gas sensing layer is fromabout 500 μm to about 3 mm.

As used herein, the term “neutral”, when used in the context ofdiscussion of the host component of a gas sensing layer and a one ormore dopant species present in the host component of the said gassensing layer refers to the situation wherein the oxidation state of thedopant species when present in the host component of the gas sensinglayer is such that the said dopant is neither p-type nor n-type.

As used herein, the term “platform”, when used in the context ofdiscussion of a gas sensing layer of a gas sensor, refers to some or allof the components of the gas sensor other than the gas sensing layeritself.

As used herein, the term “harsh environment” or “harsh environments”refers to an environment within a volume that is in the vicinity of thegas sensing layer, and in which are present the analytes whose detectionand/or estimation is being sought. The temperature within this volumemay not be uniform, i.e., the temperature at/of different locationswithin this volume can be different, and can be from about 200° C. toabout 800° C. Present at different locations within this volume can bedifferent amounts of corrosive chemical species including but notlimited to NO_(x), SO_(x), H₂O, particulate matter, hydrocarbons, and acombination thereof.

As used herein, the term “response modification layer” refers to a layerwhich serves to introduce dopants into a gas sensing layer via surfacedoping through the mechanism of diffusion. This surface doping mayresult in a modification of the response of the gas sensing layer for agiven set of operating parameters and/or operating environments.

As used herein, the term “glass” refers to any suitable material thatmay be used to form a separating layer, that in a given embodiment ofthe gas sensor, has sufficient thermal conductivity to provide asufficiently large heat link between the elements that the separatinglayer segregates, and which has sufficient electrical resistivity toprovide sufficient electrical resistance between the elements that theseparating layer segregates.

A gas sensor can be any device capable of producing an electrical signalproportional to a response characteristic that can be modulated uponexposure to gases. Examples of suitable devices include, but are notlimited to, a resistor, a field effect transistor, a capacitor, a diode,and a combination thereof.

Examples of suitable gases to be sensed include, but are not limited to,NO, NO₂, SO_(x), O₂, H₂O, NH₃, CO, and combinations thereof. In oneembodiment, the gas sensor may not be susceptible to poisoning by SO₂and CO₂ gases.

Referring to the drawings in general and to FIG. 1 in particular, itwill be understood that the illustrations are for the purpose ofdescribing a preferred embodiment of the invention and are not intendedto limit the invention thereto.

FIG. 1 is a diagrammatical representation of one embodiment of a gassensor 100 that may be used to detect an analyte. Although, NO_(x) isused as an example with respect to some of the embodiments described,note that the gas sensor may be useful to detect other analytes, suchas, for example, O₂, H₂O, CO, SO_(x), NH₃, and combinations thereof. Thegas sensor 100 might be, for example, an in-situ gas sensor thatdirectly samples a gas stream to be analyzed. In this way, the gassensor 100 can be exposed to the gas stream and generate a detectionsignal indicating whether a particular analyte (e.g., NO_(x)) ispresent. The gas sensor 100 can also generate a signal proportional tothe concentration of the analyte and thereby measure the concentrationof the analyte.

The illustrated embodiment 100 includes a substrate 102. On thissubstrate layer is disposed a heater 104. A first glass layer 106 ispositioned above the heater 104. On the first glass layer 106 isdisposed a temperature sensing layer 108. A second glass layer 110 ispositioned above the temperature sensing layer 108. On the second glasslayer 110 is disposed at least one electrode 112. An adhesion layer 114completely covers the at least one electrode 112, and also is in contactwith the second glass layer 110. A response modification layer 116 isdisposed onto the adhesion layer 114. Upon this response modificationlayer 116 is disposed a gas sensing layer 118 which has a gas sensingsurface 120. In some embodiments, the gas sensor 100 may include anelement for heating the gas sensor. In one embodiment, an element forheating the gas sensor 100 may be disposed adjacent to the gas sensinglayer 118, or it may be embedded within the gas sensing layer, oradjacent to the substrate layer 102, or on the packaging and anycombinations thereof, and/or be covered with an electrically insulatingand thermally conducting layer. The heater 104 may be an element that isseparate from the main gas sensor 100, such as a metal (e.g., Pt) layerdisposed adjacent to the gas sensing layer 118. The heater 104 may alsobe the gas sensing layer 118 itself. In one non-limiting example, alarge current may be passed through the gas sensing layer in order toheat it to a desired temperature. The addition of heat, to the surface120 of the gas sensing layer 118 also may result in faster response andrecovery times. Not to be limited by any particular theory, it isbelieved that the heat decreases the resident time of each gas speciesat the surface 120 of the gas sensing layer 118. The heater 104 may alsoallow for adjusting the temperature of the gas sensor 100 to allow forhigher sensitivity to gas species that are predisposed to superiordetection at higher temperature ranges even when the gas streamenvironment to be measured has not reached such temperatures. This maybe important in such applications that require gas sensing when anengine has only recently been started. Keeping the gas sensor 100 at aconstant temperature, such as the maximum operable temperature, also canbe used to ignore any dependence of the response signal on temperature,thus, allowing for simpler interpretation of the response signal.Additionally, the heating of the gas sensor 100 may be intentionallymodified to provide a selective response to a variety of gases as drivenby the temperature dependent selectivity and/or sensitivity of the gassensing layer 118 to one or more species of analyte. Selectivity as usedherein, refers to the ability of a gas sensor to discriminate betweendifferent presented analyte species. Sensitivity as used herein, refersto the ability of a gas sensor to display a change in an electricalcharacteristic when an analyte is presented to it. Selectivity,therefore, may be due to differing sensitivities towards differentanalyte species.

In one embodiment, the gas sensing layer 118, may in the form of a thinfilm. In another embodiment, the gas sensing layer 118, may be in theform of a thick film. In yet another embodiment, the gas sensing layer118, may be in the form of a pellet.

In one embodiment, a catalyst layer may be disposed adjacent to the gassensing layer. Such a catalyst layer may aid in the chemical conversionof one or more analyte species, into one or more analyte species whichare amenable to detection by the said gas sensing layer. Suitablematerials from which said catalyst layer may be composed include, butare not Limited to, Pt, RuO₂, and combinations thereof.

In one embodiment, the substrate 102 shown in FIG. 1 may be composed ofalumna. In another embodiment, the substrate 102 shown in FIG. 1 may becomposed of yttria stabilized zirconia (YSZ). In yet another embodiment,the substrate 102 may be composed of zirconia.

The glass layers 106 and 110 are layers of thermally conducting butelectrically insulating materials that are interposed between the heater104 and temperature sensing layer 108, and between the temperaturesensing layer 108 on one side and the at least one of the electrode 112and adhesion layer 114 on the other side, respectively. Such glasslayers 106 and 110, composed of such thermally conducting butelectrically insulating materials, allow heat to be transported acrossthe gas sensor 100, yet inhibit electrical contact between the heater104 and the temperature sensing layer 108, and between the temperaturesensing layer 108 on one side and the at least one of the electrodes 112and adhesion layer 114 on the other side, respectively. Examples ofsuitable materials for the glass layers 106, 110 include, but are notlimited to, polysilicate glass, silicon dioxide, silicon nitride, andany combinations thereof. The glass layer 110 may also be subjected tophysical and chemical treatments to enable enhanced physical adhesion ofthe at least one electrode 112 and adhesion layer 114 to itself.Further, varying thicknesses of glass layers 106, 110 should allow fordifferent amounts of heat links and electrical resistances between theirrespective enclosing layers.

In one embodiment, the dopant in the gas sensing layer 118 may beselected from the group consisting of Li, Na, K, Rb, Cs, Mg, Ca, Sr, Ba,V, Cu, Zr, Hf, Al, Si, P, Tb, Ti, Mn, Fe, Co, Ni, Zn, Y, Nb, Mo, Ru, Rh,Pd, La, Ta, W, Ga, In, Sb, Bi, Ce, Sm, Gd, Cd, Re, Pt, Ge, Cr, Pb, Lu,Nd, Pr, Eu, and combinations thereof. In another embodiment, the dopantin the gas sensing layer 118 can be selected from the group consistingof Re, Ni, V, Ta, Nb, Mo, Zr, and combinations thereof.

In one embodiment, the oxidation state of the one or more dopantspecies, when present in the host component of the gas sensing layer,may be such that the one or more dopant species are of n-type, p-type,or neutral type, or combinations thereof. Examples of such (host,dopant) pairs, wherein the dopant is of n-type may include, but are notlimited to (tantalum oxide, Re and/or Cr), (tungsten oxide, Re and/orMn). Examples of such (host, dopant) pairs, wherein the dopant is ofp-type may include, but are not limited to (tantalum oxide, Zr and/orHf), (tungsten oxide, Ta and/or Nb and/or V). Examples of such (host,dopant) pairs, wherein the dopant is of neutral type may include, butare not limited to (tantalum oxide, Nb), (tungsten oxide, Mo).

In one embodiment, the gas sensing layer may be composed of more thanone material selected from the group represented by the chemical formulaL_(α)M_(β)O_(γ), wherein L is a chemical element selected from the groupconsisting of Li, Na, K, Rb, Cs, Mg, Ca, Sr, Ba, V, Cu, Zr, Hf, Al, Si,P, Tb, and combinations thereof, and M is a chemical element selectedfrom the group consisting of Ti, Mn, Fe, Co, Ni, Zn, Y, Nb, Mo, Ru, La,Ta, W, Ga, In, Sn, Sb, Bi, Ce, Sm, Gd, and combinations thereof, and α,β, γ, are self-consistent. Examples of suitable materials from which thegas sensing layer may be composed include, but are not limited to,Ta₂O₅, Tb₃FesO₂, La_(0.8)Sr_(0.2)MnO₃. In one embodiment, the gassensing layer may be composed of more than one metal oxide compound,wherein the said metal is selected from the group consisting of W, Ta,and Nb. In the situation wherein the said gas sensing layer is composedof more than one material, the more than one material together may bepresent in forms, including but not limited to, mixture, solid solution,and combinations thereof. Suitable non-limiting examples of suchmixtures include CeO₂—Sm₂O₃.

In one embodiment, when the gas sensing layer of the gas sensor iscomposed of a material represented by the chemical formulaL_(α)M_(β)O_(γ), enhanced NO_(x) response characteristics may beobtained for particular choice of L and M.

In one embodiment, when the gas sensing layer of the gas sensor iscomposed of a material represented by the chemical formulaL_(α)M_(β)O_(γ) enhanced NO_(x) response characteristics may be obtainedfor particular choice of L and M, and for particular amounts, α and β,of L and M respectively.

In one example, the response characteristics of the gas sensor to agiven concentration of at least one analyte may be enhanced by varyingthe thickness and/or porosity of the gas sensing layer, when it is inthe form of a thin film. In one embodiment, the thin film gas sensinglayer 118 can have a thickness from about 10 nm to about 500 nm. Inanother embodiment, the thin film gas sensing layer 118 can have athickness from about 50 nm to about 150 nm. In yet another embodiment,the thin film gas sensing layer 118 can have a thickness from about 70nm to about 120 nm.

In one example, the response characteristics of the gas sensor 100 to agiven concentration of at least one analyte may be enhanced by varyingthe thickness and/or porosity of the gas sensing layer 118, when it isin the form of a thick film. In one embodiment, the said thick film gassensing layer 118 can have a thickness from about 500 nm to about 500μm. In another embodiment, the said thick film gas sensing layer 118 canhave a thickness from about 10 μm to about 300 μm. In yet anotherembodiment, the said thick film gas sensing layer 118 can have athickness from about 20 μm to about 200 μm.

In one example, the response characteristics of the gas sensor 100 to agiven concentration of at least one analyte may be enhanced by varyingthe thickness and/or porosity of the gas sensing layer 118, when it isin the form of a pellet. In one embodiment, the pellet gas sensing layer118 can have a thickness from about 500 μm to about 3 mm. In anotherembodiment, the pellet gas sensing layer 118 can have a thickness fromabout 1 mm to about 3 mm. In yet another embodiment, the pellet gassensing layer 118 can have a thickness from about 1 mm to about 2 mm.

In one embodiment, the response of the gas sensor, or of the materialcomposing a sensing layer of the gas sensor, may be monitored viaresistive measurement, potentiomnetric measurement, thermal measurement,or combinations thereof. The said thermal measurement, may be performedvia several techniques, including but not limited to thermal imaging viainfra-red camera.

A response modification layer 116 is interposed between the gas sensinglayer 118 and the adhesion layer 114. In one embodiment, this responsemodification layer 116 may be composed of a material selected from thegroup consisting of Mg, V, Cu, Zr, Hf, Al, Si, Ti, Mn, Fe, Co, Ni, Zn,Nb, Mo, Ru, Rh, Pd, La, Ta, W, In, Sn, Sb, Bi, Sm, Re, Pt, Ge, Cr, andcombinations thereof. In another embodiment, this response modificationlayer 116 may be composed of a material selected from the groupconsisting of Ti, Re, Ni, Ta, Nb, Mo, Zr, and combinations thereof. Inone embodiment, the response modification layer 116 can have a thicknessfrom about 10 Å to about 100 Å. In another embodiment, the responsemodification layer 116 can have a thickness from about 20 Å to about 80Å. In yet another embodiment, the response modification layer 116 canhave a thickness from about 30 Å to about 60 Å. In one embodiment of thegas sensor, the response modification layer may aid the gas sensor inhaving an equisensitive response to any two given gases. In anotherembodiment of the gas sensor 100, the response modification layer 116may aid the gas sensor in having a desired value of baseline resistance.In yet another embodiment, the response modification layer may aid thegas sensor 100 in having a desired level of stability of baselineresistance with exposure over time to one or more analytes. In yetanother embodiment of the gas sensor 100, the response modificationlayer 116 may aid the gas sensor in having desired levels of responseand recovery times upon exposure to and withdrawal of analyterespectively. Not to be limited by any particular theory, it is possiblethat the response modification layer 116 helps improve the workingcharacteristics of the gas sensor 100 by preventing direct physicalcontact between the gas sensing layer 118 and the adhesion layer 114.

In one embodiment, the response modification layer 116 may be composedof a mixture of Ti with at least one chemical element selected from thegroup consisting of Mg, V, Cu, Zr, Hf, Al, Si, Mn, Fo, Co, Ni, Zn, Nb,Mo, Ru, Rh, Pd, La, Ta, W, In, Sn, Sb, Bi, Sm, Re, Pt, Ge, Cr, andcombinations thereof.

The adhesion layer 114 serves to anchor the response modification layer116, upon which is disposed the gas sensing layer 118. The adhesionlayer 114 may be composed of at least one chemical element selected fromthe group Ti, Cr, and combinations thereof. In one embodiment, theadhesion layer 114 can have a thickness from about 5 Å to about 100 Å.In another embodiment, the adhesion layer 114 can have a thickness fromabout 10 Å to about 50 Å. In yet another embodiment, the adhesion layer114 can have a thickness from about 15 Å to about 30 Å.

The at least one of the electrodes 112 may be made from any materialcapable of physical adhesion and electrical contact to its adjacentlayers. Examples of suitable materials for the at least one electrode112 include, but are not limited to, Pt, Pd, Au, Ag, Ni, Ti, In, Sn, Cr,nickel oxide, nickel nitride, titanium nitride, aluminum doped zincoxide, indium tin oxide, and any combination thereof.

In one embodiment, the at least one of the electrodes 112 can have athickness from about 500 Å to about 10000 Å. In another embodiment, theat least one of the electrodes 112 can have a thickness from about 800 Åto about 3000 Å.

In one embodiment, the at least one of the electrode 112 may be amultilayer stack of materials. Examples of suitable materials tocomprise the different layers of the multilayer stack include, but arenot limited to, Pt, Pd, Ti, Al, Au, Ag, Ni, Cr, In, titanium nitride,nickel oxide, aluminum doped zinc oxide, nickel nitride, indium tinoxide, chrome, and any combination thereof.

In one embodiment in which the at least one of the electrodes 112 is amultilayer stack of materials, the thickness of each layer can be fromabout 100 Å to about 2000 Å. In another embodiment, in which the atleast one of the electrodes is a multilayer stack of materials, thethickness of each layer can be from about 300 Å to about 1500 Å. In yetanother embodiment, in which the at least one of the electrodes 112 is amultilayer stack of materials, the thickness of each layer can be fromabout 500 Å to about 1000 Å.

In one embodiment, the at least one of the electrodes 112 can be placedin an interdigitated geometry 202 as shown in the gas sensor 200 in FIG.2. Element 204 shows the geometry of underlying heater 104. In anotherembodiment, the at least one of the electrodes 112 can be placed in aninline geometry 302 as illustrated in the gas sensor 300 in FIG. 3.Element 304 shows the geometry of underlying heater 104.

In one embodiment, the at least one electrode 112 may be placed adjacentto the gas sensing layer 118 in a “sandwich” geometry, i.e., the atleast one electrode 112 is disposed on either side of the gas sensinglayer 118 along its thickness direction. In another embodiment, the atleast one electrode 112 may be placed in a “side-by-side” geometry,i.e., at least two electrodes are disposed adjacent each other on thesame side of the gas sensing layer 118. In another embodiment, aadhesion layer may be placed along those surfaces of the at least oneelectrode 112 that are closest to adjacent components of the gas sensor100.

In one embodiment, the gas sensing layer 118 can have a dopantconcentration from about 0 mol % to about 5 mol %. In anotherembodiment, the gas sensing layer 118 can have a dopant concentrationfrom about 0.01 mol % to about 5 mol %. In yet another embodiment, thegas sensing layer 118 can have a dopant concentration from about 0.2 mol% to about 5 mol %. In yet another embodiment, the gas sensing layer 118can have a dopant concentration from about 0.5 mol % to about 4 mol %.In yet another embodiment, the gas sensing layer 118 can have a dopantconcentration from about 1 mol % to about 3 mol %.

In some embodiments, the gas sensor may include a way of measuring thetemperature of the device. A means of measuring the temperature may bedisposed anywhere within or close to the gas sensor. For example, it maybe disposed adjacent to the gas sensing layer or, adjacent to thesubstrate layer, or on the packaging, or any combination thereof, and/orbe covered with an electrically insulating and thermally conductinglayer. Examples of temperature sensors include, but are not limited to,a resistive temperature device, a thermocouple, a silicon bandgaptemperature sensor, a thermistor, infra-red camera, and combinationsthereof. The temperature sensing means may be a separate element, suchas a metal (e.g., Pt) layer disposed adjacent to the gas sensing layer.

The thermocouple temperature sensor can be of various types, includingbut not limited to Type K (CHROMEL®/ALUMEL®), Type J (Iron/Constantan),Type N (NICROSIL®), Type B, Type R, Type S, Type T (Copper/Constantan),Type C. The resistance temperature sensor can be composed of variousmetals, but are usually made from Pt. The silicon bandgap temperaturesensor can be composed of pure silicon or of chemical compounds ofsilicon including, but not limited to, silicon carbide. The thermistortemperature sensor can be composed of various materials including butnot limited to ceramics and polymers. These materials can have apositive or a negative temperature coefficient of resistance. Thetemperature sensors may be biased in various ways, including but notlimited to, voltage biasing and current biasing. Furthermore, theresponse of the temperature sensors may be recorded by means includingbut not limited to resistive measurement, potentiometric measurement anda combination thereof.

Other gas sensor operating and geometry parameters being fixed, theresponse to a given concentration of any particular analyte may beoptimal when the gas sensing layer is maintained at particulartemperatures. In certain embodiments, optimal sensitivity may beachieved by maintaining the temperature within the range from about 300°C. to about 550° C.

Conceivably, different applied direct current (DC), alternating current(AC), or a combination thereof, of bias levels to the gas sensing layermay optimize the gas sensing characteristics such as selectivity andsensitivity towards one or another analyte. For example, according tosome embodiments, varying levels of a DC bias may be used to adjust thesensitivity of the gas sensor 100 to different gas species in ananalyte. For example, a gas sensor operating under a given first DC biaslevel might be preferentially sensitive to a first analyte species, agas sensor operating under a second DC bias level might bepreferentially sensitive to a second analyte species, and so on fordifferent DC bias levels. This property may be used to selectivelydetect and measure different species of analyte. The AC and/or DC biasused in the operation of the gas sensor may be an electrical current, anelectrical voltage or a combination thereof. The AC or DC response ofthe gas sensor during operation of the gas sensor may be an electricalcurrent, an electrical voltage or a combination thereof.

The gas sensor also may be configured to have suitable filters thatallow only specific analytes to pass through and impinge onto, i.e.,make contact with, the gas sensing layer. Conceivably, such filter(s)may aid selective detection of given one or more analytes. Suchfilter(s) also may aid in limiting the passage of certain analytes suchas, for instance, particulate matter, towards the gas sensing layer. Insome embodiments, membranes that serve as filters towards particularchemical or physical species present in the environment of the gassensor may be disposed adjacent to the gas sensing layer. Such filterswould provide a means for limiting or regulating the type and/or theamount of gas or particulate species that contact the gas sensing layerof the gas sensor. Examples of suitable means for limiting or regulatingthe type and/or amount of gas species include, but are not limited to, athin film porous membrane filter medium (e.g., steel wool or quartzwool), an about 10 Å thick film of Pd, porous ceramic materials such asAl₂O₃, YSZ, SiO₂, and any combinations thereof. Conceivably, more thanone gas sensor may be placed adjacent to each other or at differentlocations within the environment. Each of these gas sensors may sharewith each other the same filter, or may individually have one or more,same or different filters. Such an “array” of gas sensors may be used toselectively detect and/or measure the concentrations of differentanalyte species at different locations within the environment.Conceivably, an “array” of more than one gas sensing layer, of same ordifferent composition, may be placed adjacent to each other, so that thesaid more than one sensing layers share the same platform, or each oneof the said more than, one sensing layers possess their own platform, orcombinations thereof.

In one embodiment, the porosity of a given gas sensing layer may betuned to that it allows one or more specified analytes to pass throughitself.

In one embodiment 400 shown in FIG. 4, the at least one electrode 112 onthe gas sensing layer 402 may be placed in a side-by-side geometry 404,and wires 406 of suitable electrically conducting material may beattached to said electrodes by suitable means. In one embodiment 500shown in FIG. 5, the at least one electrode 112 on the gas sensing layer502 may be placed in an embedded geometry 504, and wires 506 of suitableelectrically conducting material may be attached to said electrodes bysuitable means. In one embodiment 600 shown in FIG. 6, the at least oneelectrode 1112 on the gas sensing layer 602 may be placed in an“extremity” geometry 604, and wires 606 of suitable electricallyconducting material may be attached to said at least one electrode bysuitable means. In one embodiment, suitable combinations of electrodegeometries of 404, 504, and 604, may be used. The said at least oneelectrode can be shaped in any suitable shape, including but not limitedto, rectangular, circular, point, and combinations thereof.

FIG. 7 is a flow chart illustrating a method 700 for manufacturing thegas sensor in accordance with an exemplary embodiment of the invention.At step 702, a substrate layer, such as substrate layer 102 is provided.At step 704, a heater layer, such as heater layer 104, is disposedadjacent to the substrate layer. At step 706, such as first glass layer106, a first glass layer is disposed adjacent to the heater layer,followed by step 708, where a temperature sensing layer, such astemperature sensing layer 108, is disposed adjacent to the glass layer.At step 710, a second glass layer, such as second glass layer 110, isdisposed adjacent to the temperature sensing layer. At step 712, atleast one electrode, such as at least one electrode 112, is disposedadjacent to the insulating layer. At step 714, a adhesion layer, such asadhesion layer 114, is disposed adjacent to the at least one electrode.At step 716 a response modification layer, such as response modificationlayer 116, is disposed adjacent to the adhesion layer. At step 718, agas sensing layer, such as gas sensing layer 118, is disposed adjacentto the response modification layer.

FIG. 8 is a flow chart illustrating a method 800 for detecting ananalyte according to an embodiment of the invention. At step 802, ananalyte is allowed to impinge upon the gas sensing layer of the gassensor causing a change in an electrical characteristic of the gassensor. In step 804, the change in the electrical characteristic, whichis being monitored continuously, is detected. If the functionalrelationship between the change in the electrical characteristic and theconcentration of the applied analyte is known, then one may determinethe concentration of the applied analyte from the measured change in theelectrical characteristic, as is shown in step 806. Examples of suitableelectrical characteristics include, but a are not limited to, electricalresistance, electrical capacitance, electrical current, electricalvoltage, and a combination thereof. As an example, if the gas sensor isused under voltage bias conditions, the electrical characteristic mightbe, for instance, electrical current. Furthermore, such response signalsmight be monitored continuously to determine information about timeevolution of concentration of an analyte.

In one embodiment, the response of the gas sensor may be tuned to beequisensitive to NO and NO₂ which are the two primary constituents ofNO_(x) emissions. The response characteristics, including but notlimited to, the response ratio of the gas sensor for differentconcentrations of NO_(x) may depend upon a plurality of systemparameters, including but not limited to, the level of oxygen deficiencyin the gas sensing layer, the one or more dopants that are doped in hostcomponent of the gas sensing layer, the level of doping of the dopant,the microstructure/morphology of the gas sensing layer, the level ofcrystallinity of the gas sensing layer, the level of strain present inthe gas sensing layer, the level of strain present in the adhesionlayer, the level of strain present in the response modification layer,the temperature at which the gas sensing layer is maintained whileperforming the gas sensing, the type and nature of the bias appliedacross the gas sensing layer, the presence or absence of the responsemodification layer, the level of adhesion of the gas sensing layer tothe electrodes and to the underlying glass, the porosity and/or packingfraction of the gas sensing layer, the porosity of the responsemodification layer, the material, size, design, and placement of theelectrodes. The microstructure/morphology of the gas sensing layer filmmay depend on the method used to grow the film. Some of the abovementioned system parameters are likely inter-related. In anotherembodiment the response characteristics, including hut not limited to,the response ratio of the gas sensor for different concentrations ofNO_(x) may depend upon a plurality of environment parameters, includingbut not limited to, the specific set of gas species that are present inthe environment and on the individual concentrations of the differentspecies present. For example, the relative humidity of the environmentwhere the gas sensor is placed, may be a factor affecting the responsecharacteristics of the gas sensor.

In one embodiment, the one or more dopants that are incorporated intothe gas sensing layer may aid in modifying one or more responsecharacteristics of the gas sensor, including but not limited to,baseline resistance, stability of baseline resistance over time,stability of baseline resistance with temperature, stability of baselineresistance over gas composition, response time, recovery time.

In the following measurements presented, the components of the sensorused may be grouped into two distinct sets depending on their source oforigin and/or procurement. The five layers, i.e., the substrate 102, theheater 104 the first glass layer 106, the temperature sensing layer 108,and the second glass layer 110 were sourced from a commercial vendor.All other elements, i.e., the electrodes 112, the adhesion layer 114,the response modification layer 116, and the gas sensing layer 118, weredesigned and implemented by the inventors.

In one embodiment, the material composing the gas sensing layer of thegas sensor was prepared in a mixture powder form according to thefollowing protocol: About 3 grams of tungsten oxide (WO_(2.9) or WO₃)powder and a required amount of powder or solution of a suitable salt ofa desired one or more dopant were taken and ground well with IPA(iso-propyl alcohol) or water in an agate pestle and mortar. Suitablesalts of the one or more dopants may include, but are not limited to,oxides, nitrates, sulphates, and carbonates. The resulting mixture wasdried at room temperature or at a temperature of about 100° C. in aoven, and a powder was obtained. This powder was heat treated in afurnace in a air/(1% H₂+N₂) atmosphere. The temperature of heattreatment was between 500° C. to 1000° C. depending on the particulardopant or dopants be incorporated into the host component of the gassensing layer. The powder was then allowed to cool to room temperatureto obtain a mixture powder of the doped tungsten oxide. In anotherembodiment, the material composing the gas sensing layer of the gassensor was prepared in a blend form according to the following protocol:About 3 grams of tungsten oxide (WO_(2.9) or WO₃) powder and therequired amount of powder or solution of a suitable salt of the desiredone or more dopant were taken and ground well with IPA or water in anagate pestle and mortar. Suitable salts may include, but are not limitedto, oxides, nitrates, sulphates, and carbonates. The resulting mixturewas dried at room temperature or at a temperature of about 100° C. in alab oven, and a blend powder of doped tungsten oxide was obtained. Thisblend powder was then allowed to cool to room temperature.

In one embodiment, a slurry of a material composing a gas sensing layerof the gas sensor was obtained as follows: about 0.126 gram ofcommercially available binder VOO6 (obtained from Heraeus™), and about0.150 gram of terpineol were mixed in a mortar and pestle, as apreviously obtained mixture powder or blend powder of doped tungstenoxide was introduced slowly. The addition of the mixture powder or blendpowder was stopped when a consistency of the slurry was optimal forscreen-printing. Not to be limited by any particular theory, the amountof doped tungsten oxide that need be introduced to obtain a slurry ofoptimal consistency, varies with size distribution of the particles fromwhich is composed the mixture powder or blend powder of the dopedtungsten oxide. Typically, the amount of doped tungsten oxide requiredto obtain a slurry of optimal consistency is from about 1.5 gram toabout 2.2 gram.

In one embodiment, a gas sensing layer of the gas sensor was depositedvia the method of screen-printing as follows: a substrate (on which arepresent Pt electrodes) was placed under a screen with optimal meshspacing and optimal mesh pore size. An optimal amount of a previouslyobtained slurry was placed on top of the substrate above the screenmesh. This slurry was forced to pass through the mesh by giving 3-5compressive movements using an evenly edged plastic screen-printingknife so that a film of the slurry was deposited on to the substrate.The screen and the substrate were now carefully separated and the slurrydeposited on the substrate was allowed to dry overnight at roomtemperature. The thus obtained deposited film was subjected to heattreatment according to the following protocol: the said film was heatedto about 300° C. at the rate of about 1° C. per minute in airatmosphere. Next the atmosphere was changed to air or (H₂+N₂), and theheating was continued at the rate of about 1° C. per minute up to amaximum processing temperature that is typically within the range fromabout 700° C. to about 1000° C. The temperature variation wasdiscontinued after the maximum processing temperature is achieved sothat the temperature was held constant for duration from about 1 hour toabout 6 hours. Subsequently, the temperature was reduced to roomtemperature at the rate of about 5° C. per minute.

The method of manufacturing of the gas sensor in an embodiment whereinthe gas sensing layer is deposited via the method of screen-printing,may be amenable for ready scaling up of production of gas sensors.Conceivably, the screen printing method of deposition of the gas sensinglayer of the gas sensor may allow for ready control of morphology of thegas sensing layer, including but not limited to factors such as porosityand packing fraction.

In another embodiment, a gas sensing layer was obtained in a pellet formas follows: a previously obtained mixture powder or blend powder wasmixed with about 2 wt % PVA (poly-vinyl alcohol) binder solution. Thethus obtained mixture was allowed to dry for an optimal amount of timeto obtain a binder mixture. A required amount of the said binder mixturewas now transferred to a suitable die, and pressed at a pressure betweenabout 4 tons to about 8 tons using a manual or hydraulic press. The thusobtained pellet was removed from the die. The obtained pellet wassubjected to heat treatment according to the following protocol: thepellet was heated to about 300° C. at the rate of about 1° C. per minutein air atmosphere. Next the atmosphere was changed to air or (H₂+N₂),and the heating was continued at the rate of about 1° C. per minute upto a maximum processing temperature that is typically within the rangefrom about 700° C. to about 1000° C. The temperature variation wasdiscontinued after the maximum processing temperature is achieved sothat the temperature was held constant for duration from about 1 hour toabout 6 hours. Subsequently, the temperature was reduced to roomtemperature at the rate of about 5° C. per minute. It is possible that avolume of the pellet undergoes a change during the said heat treatment.

In one embodiment, the porosity, and size and shape of the particlescomposing the powders that are used in the manufacture of the gassensing layer of the gas sensor may influence the responsecharacteristics of the gas sensor, including but not limited to,selectivity towards one or more analytes, sensitivity towards one ormore analytes, response time upon exposure to one or more analytes,recovery time upon withdrawal of one or more analytes, baselineresistance, stability of baseline resistance, response ratio.

In some embodiments of the gas sensor, the host component of the gassensing layer was composed of tungsten oxide. Typically, the powdersthat were used to form the said gas sensing layer had the compositionWO_(2.9) or WO₃. Typically, the powders of composition WO_(2.9) weresourced from a commercial vendor and had a particle size (diameter)distribution that was unimodal, with mean value of about 34.8 μm andstandard deviation of about 17.4 μm. On the other hand, the powders ofcomposition WO₃ were sourced either from a commercial vendor, or wereprepared in-house. The commercially sourced powders of composition WO₃had a particle size distribution that was bimodal, with the two peaksbeing placed at about 5 μm and at about 12 μm. The homemade powders ofcomposition WO₃ were obtained by pyrolysis of H₂WO₄ at about 500° C.,and had a particle size distribution that was unimodal, with mean valueof about 1.2 μm and standard deviation of about 0.6 μm.

Not to be limited by any particular theory, it is believed that responsecharacteristics of the gas sensor, including but not limited to,response time, recovery time, and the sensitivity of the gas sensor toany given one or more analytes may be a function of the packing fractionof the gas sensing layer.

In one embodiment, the gas sensing layer as deposited may be subjectedto annealing in the presence of hydrogen gas. Not to be limited to anyparticular theory, the said annealing in the presence of hydrogen mayresult in a loss of adhesion of the gas sensing layer on the adjacentlayers in contact with itself.

In one embodiment, a certain amount of diffusion is expected to takeplace within the different layers constituting the gas sensor, i.e.,adjacent layers may diffuse into each other where they meet.

The following results of measurements of the response of certainembodiments of the gas sensor were performed according to the followingprotocol: a mixture gas comprised of gases O₂ and N₂, in an ratio of 1:9is made to flow within the chamber where the gas sensor is mounted. Theflow rate of mixture gas is typically 1 slm (standard liters perminute). Specified amount between about 5 ppm to about 500 ppm of NO_(x)gas are then introduced into the said flow for durations typicallybetween 5 minutes to about 10 minutes. The response of the gas sensor,which is maintained at a temperature of about 400° C., is continuouslymonitored. Typically, the above measurements of response of the gassensor are performed for a duration of about 72 hours. The response timeis obtained from the time evolution of the response upon theintroduction of the NO gas in to the sample chamber. The recovery timeis determined in similar vein by switching off of the flow of the NOgas, all other conditions remaining identical. The flow of NO iswithdrawn, typically for duration 20 or 30 minutes. The recovery time isobtained from the time evolution of the response upon the withdrawal ofthe NO gas in to the sample chamber. This sequence of steps may berepeated to determine the reproducibility of the response.

In one embodiment, the gas sensing layer of the gas sensor may need tobe conditioned before it displays a desired and/or adequate response toany given one (or more) analyte(s). For example, when the method ofdeposition of the gas sensing layer is sputtering, then the as-depositedgas sensing layer is likely amorphous. This as-deposited gas sensinglayer may not display desired or adequate response characteristics to,say, NO_(x). Not to be limited by any particular theory, it is believedthat changing the morphology of the gas sensing layer to tune its levelof crystallinity, and/or grain size, and/or grain boundaryinterconnectivity, and/or porosity, and/or packing fraction and/orpacking density, amongst other factors, will result in improved responsecharacteristics of the gas sensor. It was determined that annealing thegas sensing layer at high temperatures in the presence of gases whichcontain nitrogen and oxygen (e.g., NO_(x)) resulted in the development,in the gas sensing layer, of desired response characteristics towardsNO_(x).

The following results of measurement of response characteristics of gassensors were obtained on gas sensing layers that were about 150 μm alonga thickness direction and in which the typical distance between theelectrodes was 1 mm. Further, the cross-section area of the gas sensinglayer, along the direction in which the resistance of the gas sensor wasmeasured, were likely approximately equal.

FIG. 9 is a graph 900 illustrating the resistance response of the gassensor over time according to an exemplary embodiment of the inventionwhen host component of the gas sensing layer is tungsten oxide that wasobtained from powder of composition WO_(2.9), and the dopant species inthe host is Re. The measurements were performed in 4-terminal mode whilepassing a fixed current equal to 100 nA (nano Ampere) between theelectrodes. Indicated levels of NO (50 ppm) and NO₂ (50 ppm) gas wereapplied successively to the gas sensor. The gas sensor was maintained ata temperature of about 400° C. when the measurements were performed. Inthis case, the response due to the presence of the first species andsecond species of analyte (NO₂ and NO respectively) induces a response(change in resistance) ratio, rr, that is, on the average, very nearly1.5. The baseline resistance is stable over time with an estimated valueof about 10000 kΩ.

FIG. 10 is a graph 1000 illustrating the resistance response of the gassensor over time according to an exemplary embodiment of the inventionwhen host component of the gas sensing layer is tungsten oxide that wasobtained from powder of composition WO_(2.9), and the dopant species inthe host is V. The measurements were performed in 4-terminal mode whilepassing a fixed current equal to 100 nA (nano Ampere) between theelectrodes. Different indicated ppm levels of NO and NO₂ gas wereapplied successively to the gas sensor. The gas sensor was maintained attemperature of about 450° C. when the measurements were performed. Inthis case, the response due to the presence of the first species andsecond species of analyte (NO₂ and NO respectively) induces a response(change in resistance) ratio, rr, that is, on the average, very nearly1.5. The baseline resistance is stable over time with a estimated valueof about 95 kΩ.

FIG. 11 is a graph 1100 illustrating the resistance response of the gassensor over time according to an exemplary embodiment of the inventionwhen host component of the gas sensing layer is tungsten oxide that wasobtained from powder of composition WO_(2.9), and there are present twodopant species in the host, namely, Re and V. The measurements wereperformed in 4-terminal mode while passing a fixed current equal to 100nA (nano Ampere) between the electrodes. Indicated levels of NO (50 ppm)and NO₂ (50 ppm) gas were applied successively to the gas sensor. Thegas sensor was maintained at temperature of about 400° C. when themeasurements were performed. In this case, the response due to thepresence of the first species and second species of analyte (NO₂ and NOrespectively) induces a response (change in resistance) ratio, rr, thatis, on the average, very nearly 2. The baseline resistance is stableover time with a estimated value of about 400 kΩ.

Not to be limited by any particular theory, it may be possible to tunethe baseline resistance of the gas sensor by incorporating suitablychosen additional dopant species within the host component of the gassensing layer of the gas sensor. For instance, comparing the baselineresistances of the gas sensors whose responses are shown in FIG. 9 andFIG. 11, one sees that when there are present 2 dopants (FIG. 11)namely, Re and V, the baseline resistance is lesser (having a estimatedvalue of about 400 kΩ) than when there is present a single dopant (FIG.9), namely Re (having a estimated value of about 10000 kΩ). In similarvein, not to be limited to any particular theory, it may be possible totune the relative stability of the baseline resistance of the gas sensorby incorporating suitably chosen additional dopant species within thehost component of the gas sensing layer of the gas sensor.

FIG. 12 is a graph 1200 illustrating the resistance response of the gassensor over time according to an exemplary embodiment of the inventionwhen host component of the gas sensing layer is tungsten oxide that wasobtained from powder of composition WO_(2.9), and there are present twodopant species in the host, namely, Zr and Re. The measurements wereperformed in 4-terminal mode while passing a fixed current equal to 100nA (nano Ampere) between the electrodes. Indicated levels of NO (50 ppm)and NO₂ (50 ppm) gas were applied successively to the gas sensor. Thegas sensor was maintained at temperature of about 400° C. when themeasurements were performed. In this case, the response due to thepresence of the first species and second species of analyte (NO₂ and NOrespectively) induces a response (change in resistance) ratio, rr, thatis, on the average, very nearly 1.5. The baseline resistance is stableover time with a estimated value of about 5000 kΩ.

FIG. 13 is a graph 1300 illustrating the resistance response of the gassensor over time according to an exemplary embodiment of the inventionwhen host component of the gas sensing layer is tungsten oxide that wasobtained from powder of composition WO_(2.9), and there are present twodopant species in the host, namely, Ta and Re. The measurements wereperformed in 4-terminal mode while passing a fixed current equal to 100nA (nano Ampere) between the electrodes. Indicated levels of NO (50 ppm)and NO₂ (50 ppm) gas were applied successively to the gas sensor. Thegas sensor was maintained at temperature of about 400° C. when themeasurements were performed. In this case, the response due to thepresence of the first species and second species of analyte (NO₂ and NOrespectively) induces a response (change in resistance) ratio, rr, thatis, on the average, very nearly 2. The baseline resistance is stableover time with a estimated value of about 7500 kΩ.

Not to be limited by any particular theory, it may be possible to tunethe response time and recovery time of the gas sensor by incorporatingsuitably chosen one or more dopant species within the host component ofthe gas sensing layer of the gas sensor. For instance, comparing therecovery time of the gas sensor whose response is shown in FIG. 9,wherein a single dopant species Re is incorporated into the hostcomponent of the gas sensing layer, to the recovery time of the gassensor whose response is shown in FIG. 12, wherein two dopant species,namely, Zr and Re, are incorporated into the host component of the gassensing layer, one sees that the recovery time is faster for the gassensor whose response is depicted in FIG. 12. In similar vein, comparingthe recovery time of the gas sensor whose response is shown in FIG. 9,wherein a single dopant species Re is incorporated into the hostcomponent of the gas sensing layer, to the recovery time of the gassensor whose response is shown in FIG. 13, wherein two dopant species,namely, Ta and Re, are incorporated into the host component of the gassensing layer, one sees that the recovery time is faster for the gassensor whose response is depicted in FIG. 13.

FIG. 14 is a graph 1400 illustrating the resistance response of the gassensor over time according to an exemplary embodiment of the inventionwhen host component of the gas sensing layer is tungsten oxide that wasobtained from powder of composition WO_(2.9), and the dopant species inthe host is V. The measurements were performed in 4-terminal mode whilepassing a fixed current equal to 100 nA (nano Ampere) between theelectrodes. Different indicated ppm levels of NO and NO₂ gas wereapplied successively to the gas sensor. The gas sensor was maintained attemperature of about 400° C. when the measurements were performed. Inthis case, the response due to the presence of the first species andsecond species of analyte (NO₂ and NO respectively) induces a response(change in resistance) ratio, rr, that is, on the average, very nearly1.5. The baseline resistance is stable over time with a estimated valueof about 400 kΩ.

FIG. 15 is a graph 1500 illustrating the resistance response of the gassensor over time according to an exemplary embodiment of the inventionwhen host component of the gas sensing layer is tungsten oxide that wasobtained from powder of composition WO_(2.9), and the dopant species inthe host is V. The measurements were performed in 4-terminal mode whilepassing a fixed current equal to 100 nA (nano Ampere) between theelectrodes. Different indicated ppm levels of NO and NO₂ gas wereapplied successively to the gas sensor. The gas sensor was maintained attemperature of about 450° C. when the measurements were performed. Inthis case, the response due to the presence of the first species andsecond species of analyte (NO₂ and NO respectively) induces a response(change in resistance) ratio, rr, that is, on the average, very nearly1.5. The baseline resistance is stable over time with a estimated valueof about 95 kΩ.

Not to be limited by any particular theory, for a given choice of one ormore dopants incorporated into the host component of the gas sensinglayer, it may be possible to tune the response characteristics of thegas sensor via the temperature at which the gas sensor is beingmaintained. For instance, comparing the baseline resistances of the gassensor, wherein a single dopant V has been incorporated into the hostcomponent of the gas sensing layer, whose responses are shown in FIG. 14and FIG. 15, one sees that when the temperature of the gas sensor ismaintained at 450° C. (FIG. 15), the estimated value of the baselineresistance is 95 kΩ, as opposed to when the temperature of the gassensor is maintained at 400° C. (FIG. 14), wherein the estimatedbaseline resistance of the gas sensor is 400 kΩ. In similar vein, it maybe possible to tune the response and recovery times of the gas sensorvia the temperature at which the gas sensor is maintained. Comparingonce again the response and recovery times of the data shown in FIG. 14and FIG. 15, one sees that the response time, as well as the recoverytime, is faster when the gas sensor is maintained at temperature ofabout 450° C. (FIG. 15) as compared to when the gas sensor is maintainedat a temperature of about 400° C. (FIG. 14). In similar vein, it may bepossible to tune the stability of the baseline resistance of the gassensor via the temperature at which the gas sensor is maintained.Comparing once again the stability of the baseline resistance of thedata shown in FIG. 14 and FIG. 15, one sees that the stability of thebaseline resistance improves when the gas sensor is maintained attemperature of about 450° C. (FIG. 15) as compared to when the gassensor is maintained at a temperature of about 400° C. (FIG. 14). Insimilar vein, comparing the baseline resistances of the gas sensor,wherein two dopants, namely, V and Re, have been incorporated into thehost component of the gas sensing layer, whose responses are shown inFIG. 16 and FIG. 17, one sees that when the temperature of the gassensor is maintained at about 450° C. (FIG. 17), the estimated value ofthe baseline resistance is 40 kΩ, as opposed to when the temperature ofthe gas sensor is maintained at about 400° C. (FIG. 16), wherein theestimated baseline resistance of the gas sensor is 150 kΩ.

It has been estimated that the delay time associated with the responseof the gas sensor as the flow of analyte is introduced/withdrawn isexpected to be within the range from about few tens of seconds to aboutfew hundreds of seconds.

In one embodiment, the gas sensor may be used to monitor and/or measurethe concentration of at least one analyte in the exhaust of an internalcombustion engine. For instance, the gas sensor may be positioned foroptimal monitoring and/or measurement of at least one analyte within theexhaust system of an automobile. In another embodiment, a plurality ofgas sensors may be positioned at different locations within the exhaustsystem of the automobile to monitor and measure the concentration ofanalytes in the exhaust. In another embodiment, the gas sensor may beused to monitor and/or measure the concentration of at least one analyteat any locations within the automobile. For instance, one or more gassensors may be positioned for optimal monitoring and/or measurement ofat least one analyte within an automobile interior.

Embodiments of the gas sensor of the present invention may also be usedto monitor emission of NO_(x) in applications including, but not limitedto, aluminum, cement, fertilizer, glass, mineral wool, power, steel,sulphuric acid, and waste incineration industries. In the automobilesector, embodiments of the gas sensor may be used to monitor emissionsin a variety of applications including, but not limited to, the emissionof NO_(x) from petrol, gasoline, diesel engine, internal combustionengine, automobiles including, but not limited to, passenger cars, lightcommercial vehicles, lorries, trucks, and buses.

The gas sensor may also be used to meet the U.S. EnvironmentalProtection Agency continuous emissions monitoring standards (CEMS)outlined in 40 C.F.R. §60 and 40 C.F.R. §75. The gas sensor may furtherbe used to meet the European Union CEN emissions limit values. Stillfurther, the gas sensors may be used in a continuous emissionsmonitoring system to determine “cap and trade” allowances as describedby local and federal regulating authorities.

In another aspect, a gas sensor is arranged within an encapsulation in aflip-chip arrangement. In a flip-chip arrangement, the gas sensor isflipped upside down, such that all of the top sensitive surface area ofthe device including the area surrounding the sensitive areas of thedevice, are protected from gases to be monitored. An additionalprotective board protects the back surface of the chip. Directly overthe sensitive area of the device, a slit, or opening in the ceramicboard to which the chip's top surface is mounted, is created to allowthe gases to flow to the gas sensing layer. A layer of high temperaturestable conductive material, such as Pt or Au, may be used tointerconnect the components of the gas sensor to leads in theencapsulation layer. This flip chip arrangement enables interconnect ina higher vibration and higher temperature, for example greater than 500°C., environments than conventional wire bonds, which are susceptible tofatigue failure. The interconnection using platinum and/or gold “bumps”to connect the components, such as the at least one of the electrodes tothe leads helps to enable the use of the gas sensor in harshenvironments.

In one embodiment the gas sensor may be configured to be operable inharsh environments in which are locations present where a temperature isbetween about 200° C. and about 800° C. In another embodiment, the gassensor may be configured to be operable in harsh environments in whichlocations are present with a temperature between about 200° C. and about600° C. In yet another embodiment, the gas sensor may be configured tobe operable in harsh environments in which are locations are presentwith a temperature between about 300° C. and about 550° C.

Embodiments of the gas sensor are cost effective in that it has a longworking life (on the order of about 1000 hours) and provides highlyrepeatable readout. The cost effectiveness is further enhanced becauseof the simple modular design of these sensors allowing ready scaling ofthe manufacturing process to large volumes.

The gas sensor may be encapsulated in a packaging. The encapsulationfurther protects the gas sensor from the high temperature and corrosiveatmosphere in the harsh environments where these sensors are likely tobe used. The encapsulation acts to cover exposed surfaces of suchelements of the device as the adhesion layer, the electrodes, the firstglass layer, the thermometer, the second glass layer, the heater, andthe substrate, which do not by themselves, sense the gases. Thisencapsulation also may involve forming a bond with the underlying layer(substrate), so as to inhibit flow of gases and corrosive materials(e.g., particulate matter, hydrocarbons) that would be detrimental tothe gas sensor over time. Examples of such suitable materials forencapsulation include, but are not limited to, silicon carbide,ceramic-based epoxies such as those containing alumina, glass, quartz,silicon nitride, silicon dioxide and a combination thereof.

The encapsulation layer can be deposited by any known method, such asplasma enhanced chemical vapor deposition (PECVD), low-pressure chemicalvapor deposition (LPCVD), and a combination thereof. The encapsulationis such that at least a portion of the gas sensing layer remains exposedto ambient gases. With the application of an encapsulation the sensorsmay be protected in harsh environments and have a longer working life.Such protection against harsh environments would allow for the use ofthese sensors in a wide variety on settings, including but not limitedto, boiling water reactor, automotive and locomotive petrol or dieselengine exhaust, industrial process (glass, aluminum, steel, andpetroleum) plant exhaust. It would further protect the gas sensor fromthe particulate matter that may be present in the exhaust streams of thepreviously mentioned environments. Such particulate matter maypotentially be detriment to the gas sensor as they may adhere to and/orcorrode the gas sensor thereby hindering the detection of exhaust gasesby hindering contact between the exhaust gases and the gas sensor.

While the invention has been described in detail in connection with onlya limited number of embodiments, it should be readily understood thatthe invention is not limited to such disclosed embodiments. Rather, theinvention can be modified to incorporate any number of variations,alterations, substitutions or equivalent arrangements not heretoforedescribed, but which are commensurate with the spirit and scope of theinvention. Additionally, while various embodiments of the invention havebeen described, it is to be understood that aspects of the invention mayinclude only some of the described embodiments. Accordingly, theinvention is not to be seen as limited by the foregoing description, butis only limited by the scope of the appended claims.

What is claimed as new and desired to be protected by Letters Patent ofthe United States is:
 1. A gas sensor, comprising: a gas sensing layer;at least one electrode; an adhesion layer; and a response modificationlayer adjacent to said gas sensing layer and said layer of adhesion. 2.The gas sensor of claim 1, wherein said gas sensing layer comprises atleast one chemical composition with a chemical formula L_(α)M_(β)O_(γ)and a dopant, wherein L is at least one element selected from the groupconsisting of Li, Na, K, Rb, Cs, Mg, Ca, Sr, Ba, V, Cu, Zr, Hf, Al, Si,P, Tb, and combinations thereof: wherein M is at least one elementselected from the group consisting of Ti, Mn, Fe, Co, Ni, Zn, Y, Nb, Mo,Ru, La, Ta, W, Ga, In, Sn, Sb, Bi, Ce, Sm, Gd, and combinations thereof;and wherein, α, β, γ, are self-consistent.
 3. The gas sensor of claim 2,wherein incorporated into the gas sensing layer is at least one dopantselected from the list consisting of Li, Na, K, Rb, Cs, Mg, Ca, Sr, Ba,V, Cu, Zr, Hf, Al, Si, P, Tb, Ti, Mn, Fe, Co, Ni, Zn, Y, Nb, Mo, Ru, Rh,Pd, La, Ta, W, Ga, In, Sb, Bi, Ce, Sm, Gd, Cd, Re, Pt, Ge, Cr, Pb, Lu,Nd, Pr, Eu, and combinations thereof.
 4. The gas sensor of claim 2,wherein α>0 only when β>0, and a≦β.
 5. The gas sensor of claim 1,wherein the said at least one electrode is positioned within theadhesion layer.
 6. The gas sensor of claim 1, wherein said adhesionlayer comprises at least one chemical element selected from the groupTi, Cr, and combinations thereof.
 7. The gas sensor of claim 1, whereinsaid response modification layer comprises at least one chemical elementselected from the group Mg, V, Cu, Zr, Hf, Al, Si. Ti, Mn, Fe, Co, Ni,Zn, Nb, Mo, Ru, Rh, Pd, La, Ta, W, In, Sn, Sb, Bi, Sm, Re, Pt, Gc, Cr,and combinations thereof.
 8. The gas sensor of claim 1, wherein said gassensing layer is capable of detecting at least one analyte selected fromthe group consisting of NO, NO₂, SO_(x), O₂, H₂O, NH₃, CO, andcombinations thereof.
 9. The gas sensor of claim 1, comprising: asubstrate layer; a heating layer adjacent to the substrate layer; afirst glass layer adjacent to the heating layer; a temperature sensinglayer adjacent to the first glass layer; and a second glass layerbetween the temperature sensing layer and the adhesion layer.
 10. Thegas sensor of claim 1, wherein said gas sensing layer is configured forequisensitive response towards two analytes selected from the groupconsisting of NO, NO₂, SO_(x), O₂, H₂O, NH₃, CO, and combinationsthereof.
 11. The sensor of claim 1, comprising a catalyst layer thataids in the conversion of one or more analyte species to one or moredifferent analyte species.
 12. The gas sensor of claim 1, wherein a gasspecies filter material is disposed adjacent to a gas sensing surface ofsaid gas sensing layer.
 13. The gas sensor of claim 1, wherein the atleast one electrode is placed in a sandwich geometry, a side-by-sidegeometry, an interdigitated geometry, a parallel geometry, orcombinations thereof.
 14. The gas sensor of claim 1, wherein said gassensor is arranged in a flip-chip arrangement.
 15. The gas sensor ofclaim 1, wherein a response of the sensor is measured using an ACdetection technique, a DC detection technique, or a combination thereof.16. The gas sensor of claim 1, wherein the at least one electrodecomprises at least two electrodes and an electrical resistance betweenthe at least two electrodes is less than about 50 MΩ.
 17. A system,comprising: an exhaust system to transport gases; and a gas sensor,comprising: a gas sensing layer; at least one electrode; an adhesionlayer; and a response modification layer adjacent to said gas sensinglayer and said layer of adhesion.
 18. The system of claim 17, whereinsaid gas sensing layer comprises at least one chemical composition witha chemical formula L_(α)M_(β)O_(γ), wherein L is at least one elementselected from the group consisting of Li, Na, K, Rb, Cs, Mg, Ca, Sr, Ba,V, Cu, Zr, Hf, Al, Si, P, Tb, and combinations thereof; wherein M is atleast one element selected from the group consisting of Ti, Mn, Fe, Co,Ni, Zn, Y, Nb, Mo, Ru, La, Ta, W, Ga, In, Sn, Sb, Bi, Ce, Sm, Gd andcombinations thereof; and wherein, α, β, γ, are self-consistent.
 19. Thegas sensing layer of claim 18, wherein a>0 only when β>0, and α≦β. 20.The system of claim 17, wherein the said system is a motorized vehicle.21-36. (canceled)